Layin Samar da Fiber Precursor
Bayani
Hanyar samar da fiber fiber precursor wanda ke ɗaukar Dimethyl Sulfoxide (DMSO) azaman ƙarfi, Acrylonitrile (AN) azaman monomer na farko, Itaconic Acid azaman monomer na biyu, AIBN a matsayin mai ƙaddamarwa don samun copolymerization na binary, da bushe-bushe jet kadi. shine babban zaɓi da aka yarda tsakanin masana fiber carbon.
Bayanan Fasaha:
A'a. | Abu | Naúrar | Ƙayyadaddun bayanai | Jawabi |
1 | Maɗaukakin layi | dtex | 1.15 | |
2 | Ƙarfin ƙarfi | CN/dtex | ≥4.0 | |
3 | Tsawaitawa | % | 12±2 | |
4 | Dimethyl Sulfoxide (DMSO) Abun ciki | % | 0.03 | |
5 | Abubuwan Mai | % | 0.5-0.1 | |
6 | Ƙarshen Ƙimar Ƙarshe | % | 3 | |
7 | Danshi Maidowa | % | ≤1 | |
8 | Bayyanar | Babu Filayen Fasasshen Fila |
Tsari:
Raw Material Shiri — → Monomer Cakuda — → Copolymerization —→ Filtar Farko — → Cire Monomer — → Tsabtace Tsakanin Sakandare —→ Tsabtace Tsakanin Batch —→ Tacewar Makamashi — → Adanawa — → Defoam — → Spinning — → Spin Bath (Primary) —→ juya wanka (Secondary) —→ Spin bath (Tertiary) —→ Tsaftace —→ Zafafawa Mai Zafi —→ Man Fetur —→ bushewa —→ Miƙewa Steam —→ Saitin Zafi —→ Maganin Antistatic — → Precursor Winding
A'a. | Abu | Naúrar | Ƙayyadaddun bayanai | Jawabi |
1 | Maɗaukakin layi | dtex | 1.15 | |
2 | Ƙarfin ƙarfi | CN/dtex | ≥4.0 | |
3 | Tsawaitawa | % | 12±2 | |
4 | Dimethyl Sulfoxide (DMSO) Abun ciki | % | <0.03 | |
5 | Abubuwan Mai | % | 0.5-0.1 | |
6 | Ƙarshen Ƙimar Ƙarshe | % | <3 | |
7 | Danshi Maidowa | % | ≤1 | |
8 | Bayyanar | Babu Filayen Fasasshen Fila |
Raw Shirye-shiryen Material -→ Cakuda Monomer - → Copolymerization -→ Tacewar Farko -→ Cire Monomer -→ Tacewar Sakandare -→ Tsabtace Batch -→ Tsabtace Tsara - → Adanawa - → Defoam - → Spinning — → Spin Bath (Primary) -→ juya wanka (Secondary) —→ Spin bath (Tertiary) —→ Tsaftace —→ Zafafawa Mai Zafi —→ Man Fetur —→ bushewa —→ Miƙewa Steam —→ Saitin Zafi —→ Maganin Antistatic — → Precursor Winding